Preparation of Nitrogen-Doped Graphene Aerogel/Epoxy Nanocomposites and Experimental Study of Mechanical Properties
سال انتشار: 1399
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 313
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ADMTL-13-4_006
تاریخ نمایه سازی: 16 دی 1399
چکیده مقاله:
Nitrogen-Doped Graphene Aerogel (N-GA) nanomaterials can significantly improve the functional efficiency of polymer composites due to its three-dimensional structure and suitable physical properties. The preparation process affects the performance improvement. In this study, the effect of preparation method and the mechanisms affecting the strength behavior of Nitrogen-doped Graphene Aerogel/Epoxy (N-GA/E) nanocomposites was investigated. For this purpose, nanoparticles of Graphene Oxide (GO) were produced using Hummers’ method; then, the N-GA was synthesized using the hydrothermal method and the freeze-drying process. The characterization experiments were used in order to confirm the structure and quality of the synthesized nanomaterials. Then, specimens of nanocomposite were prepared by adding weight percentages of 0.05, 0.1, 0.2, 0.5, 1, and 2 from the synthesized N-GA to the epoxy resin. In other preparation processes, N-GA/E nanocomposite specimens were produced using auxiliary solvents. After tensile tests, the best strength performance was observed in the specimens with the preparation process in which acetone solvent was used. The tensile strength and modulus of these nanocomposite specimens have increased by 23% and 20% compared to neat epoxy specimens, respectively. Also, the optimal weight percentage of N-GA nanomaterials for distribution in epoxy is 0.1 wt.%. Microscopic images of the fracture surfaces of the specimens used in the tensile test showed that the placement of N-GA porous plates in epoxy with the creation of the mechanism for micro crack formation led to more energy absorption during the stretching process of the N-GA/E nanocomposites.
کلیدواژه ها:
Nitrogen-Doped Graphene Aerogel ، nanocomposite ، Morphology of Fracture Surfaces ، Tensile Properties
نویسندگان
ali kordi
Department of Mechanical Engineering, Science and Research Branch, Islamic Azad University, Tehran, Iran
saeed adibnazari
Department of Aerospace Engineering, Sharif University of Technology, Tehran, Iran
Ali Imam
Department of Mechanical Engineering, Science and Research Branch, Islamic Azad University, Tehran, Iran
mohammad najafi
Department of Mechanical Engineering, Science and Research Branch, Islamic Azad University, Tehran, Iran
maryam ghasabzadeh saryazdi
Vehicle Technology Research Institute, Amirkabir University of Technology, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :