M. Ershadi Khameneh - Department of Materials Engineering, Tarbiat Modares University, P.O. Box ۱۴۱۱۵-۱۴۳, Tehran, Iran
H. Shahverdi - Department of Materials Engineering, Tarbiat Modares University, P.O. Box ۱۴۱۱۵-۱۴۳, Tehran, Iran
M. M. Hadavi

Creep age forming (CAF) is one of the novel methods in aerospace industry that has been used to manufacture components of panels with improved mechanical properties and reduced fabrication cost. CAF is a combined age-hardening and stress-relaxation that are responsible for strengthening and forming, respectively. This paper deals with the experimental investigations of mechanical and springback properties of Al-Zn-Mg Al alloy in creep forming process. Creep forming experiments have been performed at temperatures of ۱۲۰◦C and ۱۸۰◦C for ۶–۷۲ h. Results indicated that yield stress and hardness of creep age formed specimens increased with increasing forming time and temperature,  simultaneously induced deflection by stress-relaxation increased. Incorporating spring back and mechanical properties, it can be found that the appropriate forming cycle was ۱۸۰ ◦C/۲۴ h among all forming conditions. CAF Time increase to a certain extent increased mechanical properties. This can be attributed to presence of stress in CAF that causes the precipitates be finer because of creation more nucleation sites. Therefor the growth of precipitates, takes place at long time and postpones the decreasing of the yield stress

creep age forming, Al-Zn-Mg alloy, age hardening, stress relaxation, mechanical properties