Hamed Bahiraei - Department of Physics, Faculty of Science, Malayer University, Malayer, Iran

NiCuZn ferrite is the most important magnetic materials used for the manufacturing of multilayer chip inductors due to its low sintering temperature (<۹۵۰°C) and good electromagnetic properties. In this study, the Ni۰.۵۰-xCuxZn۰.۵Fe۲O۴ nanopowders with different Cu contents (x=۰.۱۵, ۰.۲۰ and ۰.۲۵) were prepared through the nitrate-citrate auto-combustion route. The prepared powders were calcined, compacted and sintered at ۹۰۰ °C for ۴ h. The structural and magnetic properties were investigated as a function of Cu content. X-ray diffraction patterns showed the formation of cubic spinel structure for all samples. A significant increase in density from ۴.۶۶ to ۴.۸۲ g/cm۳ were observed with increasing Cu content. The microstructural evaluations revealed that Cu can affect the densification and porosity of the samples. The electromagnetic results revealed that the magnetic permeability increased with Cu content and the highest value of ۱۶۱ was obtained at x = ۰.۲۵.

Nanocrystalline materials, ferrite, Electroceramics, Initial permeability