Effect of Zr on the microstructure of 6061 Aluminum alloy during SIMA process
عنوان مقاله: Effect of Zr on the microstructure of 6061 Aluminum alloy during SIMA process
شناسه ملی مقاله: IIAC03_031
منتشر شده در سومین کنفرانس بینالمللی آلومینیوم ایران IIAC2014 در سال 1393
شناسه ملی مقاله: IIAC03_031
منتشر شده در سومین کنفرانس بینالمللی آلومینیوم ایران IIAC2014 در سال 1393
مشخصات نویسندگان مقاله:
r khorsihdi - School of Materials and Metallurgy Engineering, College of Engineering, University of Tehran, Tehran, Iran
m emamy - School of Materials and Metallurgy Engineering, College of Engineering, University of Tehran, Tehran, Iran
a akrami - School of Materials and Metallurgy Engineering, College of Engineering, University of Tehran, Tehran, Iran
m amuei - School of Materials and Metallurgy Engineering, College of Engineering, University of Tehran, Tehran, Iran
خلاصه مقاله:
r khorsihdi - School of Materials and Metallurgy Engineering, College of Engineering, University of Tehran, Tehran, Iran
m emamy - School of Materials and Metallurgy Engineering, College of Engineering, University of Tehran, Tehran, Iran
a akrami - School of Materials and Metallurgy Engineering, College of Engineering, University of Tehran, Tehran, Iran
m amuei - School of Materials and Metallurgy Engineering, College of Engineering, University of Tehran, Tehran, Iran
In this study the effect of adding Zr on the microstructure of 6061 Al alloy during SIMA process has been investigated. The optimum amount of Zr containing master alloy for proper grain refining was obtained as 0.3 wt.%. After that SIMA process employed hydraulic press, recrystallization and partial melting (RAP) to obtain a fine globular microstructure. 40% strain, various heat treatment temperatures (605 to 645°C) and holding times (30 and 40 minutes) were investigated to reach an optimized fine globular microstructure. Microstructural study which was carried out bythe optical microscopy and MIP software exhibited the uniform equiaxed recrystallized grain structure. Observations showed that the presence of grain refining agents lead to finer distribution of intermetallics and more globular microstructure during SIMA process
کلمات کلیدی: Aluminium; 6061 Alloy; SIMA; Grain Refinement; Recrystallization