In Vitro Evaluation of the Effect of SP200 Lubricant on Compressive Strength of Lightweight Concrete with Leca Aggregate and Powdered Silica
سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 561
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JCEMA-3-4_004
تاریخ نمایه سازی: 31 خرداد 1399
چکیده مقاله:
In today s advanced world and due to advances in various scientific fields of the concrete, industry has also evolved, and light concrete production is a result of these advances. It has had its advantages, many efforts have been made in the past to improve the quality and efficiency of concrete, and today the use of additives helps us to achieve this goal. The additive in this study is lubricant based on polycarboxylate brand SP200 and Powdered silica. The use of silica is also widely used in advanced countries due to its pozzolanic properties. In this study of 20 mixing designs, 2 of which were used as control sample and 18 with SP200 super-lubricant and micro silica powder, the results show that in the first mixing design with 0.49 water/cement ratio the highest compressive strength of The 7 and 28 days is related to M / 35/5 sample which has 0.35% super-lubricant and 5% micro silica powder And in the second mixing scheme with water/cement ratio of 0.55, the highest compressive strength is related to the sample of M /35/10 It contains 0.35% super-lubricant and 10% Powdered silica. The use of silica and super-lubricant in the manufacture of lightweight concrete has increased the compressive strength of lightweight concrete in some of the samples.
کلیدواژه ها:
نویسندگان
Neda Mohammadi
Building Materials Institute, Apadana Institute of Higher Education, Shiraz, Iran.
Davood Ghaedian Ronizi
Department of Civil Engineering, Eghlid Branch, Islamic Azad University, Shiraz, Iran.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :