Experimental study on fracture behavior of rubber-toughened epoxy in bulk and laminated composite specimens
محل انتشار: دومین کنفرانس بین المللی کامپوزیت
سال انتشار: 1389
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,657
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
COMPOSIT02_015
تاریخ نمایه سازی: 24 مهر 1389
چکیده مقاله:
To study the toughening mechanisms of liquid rubber (LR) in bulk epoxy and laminated composite, experimental investigations were carried out on single-edge notched bending (SENB), double-cantilever-beam (DCB) and end notch flexure (ENF) specimens under mode-I and II loading. The matrix materials were pure epoxy (bisphenol A) and LR (ATBN, CTBN, VTBN) modified epoxies. The results showed that using rubber particles would improve fracture toughness of neat epoxy resin and laminated composites. The behavior of the composite was affected by the pattern that the particles are spread in resin or the final laminated composite. Inappropriate spread of the particles would decrease the fracture toughness in some cases. However, if they are spreaded perfectly, they will improve the composite resistance against fracture. The modulus, E, of the epoxy polymer decreases with the addition of the LR. Of course, these relatively minor changes in these properties of the rubber-toughened epoxy polymer are more than compensated for by the significant increases in the fracture toghness value. The poor toughness behavior of CTBN in the glass fiber laminate was thought to be caused by the concentration of LR particles in the resin-fiber bonding surface. Morphographs of the fracture surfaces also testified this prospect.
کلیدواژه ها:
epoxy-glass composites-delamination-fracture toughness-toughening additives
نویسندگان
H Pakdel
Graduate student
M Abbasi
Geaduate student
M.A Kuchakzadeh
Professor, Department of Aerospace Engineering
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :