Microstructure Investigation and Mechanical Properties of Resistance Upset Butt Welded Ti-6Al-4V Alloy
سال انتشار: 1399
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 238
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ADMTL-13-3_010
تاریخ نمایه سازی: 16 دی 1399
چکیده مقاله:
In the present study, resistance upset butt welding was used as a solid-state process for joining Ti-6Al-4V alloy. Results showed that melting and subsequent solidification of the alloy at the joint interface promoted the development of a cast microstructure along with some pores. However, by applying the constant upset pressure of 1.62 MPa, the pore volume fraction decreased considerably with decreasing the welding current from 110 A/mm2 to 55 A/mm2. Hardness test results showed that the weld interface and the base material had the highest (352 HV) and the lowest (318 HV) values, respectively. The microstructure of the interface consisted of ά martensite and Widmanstätten laths. The tensile strength of the joints varied between 550 and 883 MPa depending on the welding parameters used. In the optimum condition, the maximum strength of the joint was about 94% of the base metal strength. Fractography of samples confirmed that the formation of pores deteriorated the strength of the joints.
کلیدواژه ها:
نویسندگان
Mahmood Sharifitabar
Department of Materials Engineering, University of Sistan and Baluchestan, Zahedan, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :