Dissolution of Nickel and Cobalt from Iron-Rich Laterite Ores Using Different Organic Acids
محل انتشار: مجله معدن و محیط زیست، دوره: 11، شماره: 3
سال انتشار: 1399
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 179
فایل این مقاله در 19 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JMAE-11-3_010
تاریخ نمایه سازی: 21 اردیبهشت 1400
چکیده مقاله:
Due to the decreasing production of nickel and cobalt from sulfide sources, the Ni and Co extraction from the oxide ores (laterites) have become more prevalent. In this research work, the effects of calcination prior to leaching, acid concentration, percent solid, pH, and stirring speed on the nickel and cobalt recoveries from an iron-rich laterite ore sample were investigated using different organic acids. Then the response surface methodology was implemented in order to optimize the various parameters. By the design of experiments, the compound optimal concentrations of the three different organic acids (gluconic acid: lactic acid: citric acid with a ratio of ۱:۲:۳) were ۳.۱۸ M, and S/L = ۰.۱, pH = ۰.۵, and the stirring speed = ۳۸۶ rpm. With the aid of kinetic studies, a temperature of ۷۵ °C, and a test time of ۱۲۰ minutes, the highest nickel and cobalt recoveries were ۲۵.۵% and ۳۷.۶%, respectively. In the optimal conditions, the contribution of the percent solids to the nickel recovery was the most and negative, after which the contribution of pH was negative, and finally, the acid concentration had a positive effect. In the optimal conditions, the acid concentration, pH, and solid content were, respectively, important in the cobalt recovery. The SEM results showed that the surface of feed and residue particles in the optimal conditions was not significantly different, and the laboratory data was fitted to a shrinking core model. The results obtained indicated that the reaction rate was controlled by the diffusion reaction at the particle surface, and the activation energies of ۱۱.۰۹ kJ/mol for nickel and ۲۸.۰۴ kJ/mol for cobalt were consistent with this conclusion
کلیدواژه ها:
نویسندگان
M. Hosseini Nasab
School of Mining Engineering, College of Engineering, University of Tehran, Tehran, Iran
M. Noaparast
School of Mining Engineering, College of Engineering, University of Tehran, Tehran, Iran
H. Abdollahi
School of Mining Engineering, College of Engineering, University of Tehran, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :