Textural Evolution of ۶۰۶۱ Aluminum Alloy Processed by Accumulative Roll-Bonding Process
محل انتشار: مجله شکل دهی مواد، دوره: 8، شماره: 3
سال انتشار: 1400
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 166
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMF-8-3_003
تاریخ نمایه سازی: 12 مرداد 1400
چکیده مقاله:
A commercial Al-Mg-Si alloy (AA ۶۰۶۱) was deformed by using the accumulative roll bonding (ARB) process for up to five cycles at ambient temperature. The evolution of texture in this process was studied by the X-ray diffraction (XRD) method. Experimental results indicate that the combination of the shear texture composed of Rotated cube {۰۰۱} component and the rolling textures that included Copper {۱۱۲} and Dillamore {۴, ۴, ۱۱}<۱۱, ۱۱, ۸> components developed after the first cycle. During the first cycle, the shear texture was developed as a result of shear deformation induced by high level of friction between the rolls and the sheet. By increasing the number of cycles, the shear texture strength diminished and changed to the rolling texture. After the fifth cycle, a remarkable increase in the rolling texture intensity was observed due to homogenous deformation induced by the presence of fine non-shearable particles. Additionally, the presence of magnesium in solid solution influenced the texture evolution during ARB.
کلیدواژه ها:
نویسندگان
Mohammad Reza Rezaei
Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran
Mohammad Reza Toroghinejad
Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran
Fakhreddin Ashrafizadeh
Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran
Hamed Asgari
Department of Mechanical Engineering, University of Saskatchewan, Saskatoon, SK S۷N ۵A۹, Canada
Jerzy Szpunar
Department of Mechanical Engineering, University of Saskatchewan, Saskatoon, SK S۷N ۵A۹, Canada
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :