Role of Etching Process of SiC Particles on the Microstructure and Mechanical Properties of Stir Casted Al۳۵۷−SiC Metal matrix Composite

Owing to their high strength-to-weight ratio, aluminum-ceramic composites, are widely used in various industries. In this study, aluminum matrix composite was fabricated with only ۲ wt% micron-sized SiC particles as the reinforcing phase using electromagnetic stir casting. Prior to mixing, the surface of SiC particles were chemically etched by HF, NaOH, and KOH at two heat treatment temperatures of ۴۶۰ and ۵۱۰ °C for ۳۰ min. The obtained results indicated better wettability and interaction between the etched SiC particles and Al matrix. In addition, etched SiC particle as a ceramic phase at ۴۶۰ °C enhanced the mechanical properties of Al as a metal matrix, such as enhancing hardness and E about of ۶.۶ and ۲۶.۶%, respectively, mainly due to the increasing inhibition against movement of dislocation confirmed by the observed brittle behavior of fracture surface.