Evaluation of Nickel and Chromium Ion Release from Stainless Steel, HANT and NiTi Arch Wires in Two ۲۸-day Time Spans
محل انتشار: دوفصلنامه ارتودنسی ایران، دوره: 10، شماره: 1
سال انتشار: 1394
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 154
نسخه کامل این مقاله ارائه نشده است و در دسترس نمی باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ORTHO-10-1_003
تاریخ نمایه سازی: 12 آبان 1400
چکیده مقاله:
Background: Stainless steel and Nickel Chromium alloys show special mechanical features, which has made them the most common materials for fabrication of orthodontic arch wires. Objectives: The aim of this study was to evaluate the effect of length of immersion and type of arch wire on release of nickel and chromium ions from fixed orthodontic appliances. Materials and Methods: ۱۵ simulated half-arch maxillary fixed orthodontic appliances were divided into ۳ groups according to the types of arch wires. Each sample was individually immersed in ۵۰ ml of distilled water and incubated at ۳۷ºC for ۲۸ days. Afterwards, solutions were sent to laboratory for investigation of the released ions and the samples were incubated for another ۲۸ days in new distilled water. After each ۲۸-day time span, the concentrations of nickel and chromium were measured using an atomic absorption spectrophotometer. T-test was used for statistical analysis and P < ۰.۰۵ were considered statistically significant. Results: Stainless steel arch wires released the greatest amount of nickel and chromium ions at both ۲۸ days periods. The lowest amount of nickel and chromium in both time spans was released from NiTi and HANT arch wires, respectively Nickel ion release decreased overtime while the chromium release increased. Conclusions: The amounts of released nickel and chromium ions from fixed orthodontic appliances from all three types of evaluated arch wires were below the daily dietary intake of these ions and do not bring about biological concerns.
کلیدواژه ها:
نویسندگان
Sepideh Arab
Department Of Orthodontics, Dental Caries Prevention Research Center, Qazvin University of Medical Sciences, Qazvin, IR Iran
Mina Hormozdiari Cham
Private Practice, Qazvin University of Medical Sciences, Qazvin, IR Iran
Marzieh Morsaghian
Department of Orthodontics, Qazvin University of Medical Sciences, Qazvin, IR Iran
Maryam Ghamari
Department Of Orthodontics, Dental Caries Prevention Research Center, Qazvin University of Medical Sciences, Qazvin, IR Iran
Omid Mortezai
Department Of Orthodontics, Dental Caries Prevention Research Center, Qazvin University of Medical Sciences, Qazvin, IR Iran