Effect of Post-Weld Intercritical Annealing on the Microstructure and Tensile Properties of a Gas Tungsten Arc Welded DP۷۰۰ Steel
محل انتشار: فصلنامه مواد پیشرفته و فرآوری، دوره: 9، شماره: 4
سال انتشار: 1400
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 82
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JMATPR-9-4_001
تاریخ نمایه سازی: 16 اسفند 1400
چکیده مقاله:
The aim of this study was to investigate the effect of post-weld intercritical annealing (IA) on the microstructure and tensile properties of a gas tungsten arc-welded DP۷۰۰ steel sheet. In this regard, DP۷۰۰ steel sheets were first joined using gas-tungsten arc welding. The welded sheet was then annealed at intercritical temperature of ۷۲۰ °C for ۱۲۰ s followed by water quenching. Microstructure and microhardness of the as-welded and post-weld heat-treated samples were characterized, as well as tensile properties. Results showed that the microstructure varied from ferrite-tempered martensite in the subcritical heat affected zone to a mixture of bainite, Widmanestatten ferrite, ferrite-carbide aggregate and grain boundary ferrite in the fusion zone. This heterogeneity in the microstructure led to the formation of hardened and softened zones across the welded joint. Strain localization in the softened zone during tensile testing resulted in a joint efficiency of ~ ۸۱% and early fracture. After post weld IA, dual phase microstructures comprising of ferrite and martensite, with different sizes and morphologies, were formed across the welded joint. This new microstructure resulted in the elimination of hardened and softened zones, which in turn led to high joint efficiency of ~ ۹۸%.
کلیدواژه ها:
نویسندگان
Hamid Ashrafi
Faculty of Chemical and Materials Engineering, Shahrood University of Technology, Shahrood, ۳۶۱۹۹۹۵۱۶۱, Iran
S.E. Aghili
Materials Engineering Group, Golpayegan College of Engineering, Isfahan University of Technology, Golpayegan ۸۷۷۱۷-۶۷۴۹۸, Iran.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :