Analysis on Effect of Fullerene Soot on the Chemical and Physical Properties of Cement Mixtures
محل انتشار: ماهنامه بین المللی مهندسی، دوره: 34، شماره: 10
سال انتشار: 1400
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 118
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJE-34-10_012
تاریخ نمایه سازی: 10 اردیبهشت 1401
چکیده مقاله:
The article reports on the relevance and the necessity of the introduction of various additives in the composition of grouting mixtures. The analysis of cement compositions with various modifications of carbon is briefly outlined. A method for obtaining fullerene soot and an analysis of its effect on the chemical and physical properties of grouting compositions made of alumina cement is presented. The physical, mechanical and operational properties of the modified grouting mixture are considered. The optimal content of carbon nanoparticles in the binder is ۰.۱-۰.۵% BWOC. The introduction of fullerene soot makes it possible to obtain high mechanical properties of cement stone (an increase in uniaxial compression strength by about ۱۵% and a decrease in porosity by about ۲۰%) in comparison with cement mix without additives. It has been determined that using carbon materials is environmentally friendly. The addition of fullerene soot to cement system does not affect the cement hydration processes, provides micro-reinforcement of the cement stone, and prevents the propagation of cracks in it at the nanoscale.
کلیدواژه ها:
نویسندگان
E. Tsigelnyuk
Department of Drilling Wells, Oil and Gas Faculty, St Petersburg Mining University, St Petersburg, Russian Federation
V. Kovalchuk
Department of Drilling Wells, Oil and Gas Faculty, St Petersburg Mining University, St Petersburg, Russian Federation
V. Gerasimov
Department of Experimental Physics, Higher school of applied physics and space technologies, Peter the Great St. Petersburg Polytechnic University (SPbPU), St Petersburg, Russian Federation
E. Efimova
ESTiUM, St Petersburg, Russian Federation
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :