Keggin-type heteropoly acid H۳PW۱۲O۴۰ supported on magnetic amine-grafted Graphene oxide: A new magnetically separable adsorbent for rapid and selective removal of cationic organic pollutants in aqueous solutions
محل انتشار: مجله بین المللی ابعاد نانو، دوره: 13، شماره: 1
سال انتشار: 1401
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 129
فایل این مقاله در 14 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJND-13-1_003
تاریخ نمایه سازی: 9 خرداد 1401
چکیده مقاله:
In the present study, phosphotungstic acid decorated on magnetic amine-grafted graphene oxide (GO-Amine/Fe۳O۴/H۳PW۱۲O۴۰; GOA/Fe۳O۴/HPW) was prepared and evaluated as a new adsorbent for removal and separation of organic dyes from water. The obtained nanocomposite was fully characterized by means of XRD, FT-IR, Raman, VSM, SEM, EDX, AFM and BET surface area analysis. The results demonstrated the successful loading of HPW (~۳۴ wt.%) on the surface of magnetic aminosilanized graphene oxide. The adsorption ability of the nanocomposite was tested towards cationic methylene blue (MB) and anionic methyl orange (MO) dyes. The nanocomposite exhibited very good adsorption performance for cationic organic pollutants; it could absorb approximately ۱۰۰% of methylene blue (MB) from an aqueous solution within only ۵ min. The removal rate of GOA/Fe۳O۴/HPW nanocomposite was greater than that of pure GOA, Fe۳O۴ and HPW. Further study revealed that the GOA/Fe۳O۴/HPW exhibited a fast adsorption rate and selective adsorption ability towards the cationic dyes from dyes mixtures.The effect of adsorbent dosage, initial concentration of dye and pH were studied in detail. Due to the existence of the Fe۳O۴, the GOA/Fe۳O۴/HPW nanocomposite could be magnetically separated from the reaction mixture and reused without any change in structure. This research could provide a new easy platform for wastewater purification.
کلیدواژه ها:
نویسندگان
Saeed Farhadi
Department of Chemistry, Lorestan University, Khorramabad ۶۸۱۵۱-۴۴۳۱۶, Iran.
Mansoureh Maleki
Department of Chemistry, Payame Noor University, Tehran ۱۹۳۹۵-۴۶۹۷, Iran.
Ladan Nirumand
Department of Chemistry, Lorestan University, Khorramabad ۶۸۱۵۱-۴۴۳۱۶, Iran.
Farzaneh Moradifard
Department of Chemistry, Lorestan University, Khorramabad ۶۸۱۵۱-۴۴۳۱۶, Iran.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :