Sol-gel synthesis, characterization, optical properties and catalytic performance of Y۲Ce۲O۷ nanomaterial
محل انتشار: مجله بین المللی ابعاد نانو، دوره: 8، شماره: 4
سال انتشار: 1396
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 105
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJND-8-4_004
تاریخ نمایه سازی: 24 تیر 1401
چکیده مقاله:
Y۲Ce۲O۷ nano powders were synthesized via sol-gel reactions at ۹۰۰ (S۱), ۱۰۰۰ (S۲) and ۱۱۰۰ (S۳) ˚C for ۴ h using yttrium acetate (C۶H۹O۶Y.xH۲O), ammonium cerium nitrate ((NH۴)۲Ce(NO۳)۶) and stearic acid (C۱۸H۳۶O۲) as raw materials at stoichiometric ۱:۱ Y:Ce molar ratio. The synthesized materials were characterized by powder X-ray diffraction (PXRD) technique and Fourier transforms infrared (FTIR) spectroscopy. Structural analysis was performed by the FullProf program employing profile matching with constant scale factors. The results showed that the patterns had a main cubic Y۲Ce۲O۷ structure with space group of Fm۳m. The data showed that the lattice parameters were increased with increasing the reaction temperature. FESEM images showed that the synthesized Y۲Ce۲O۷ particles had mono-shaped sphere morphologies. However, with increasing the reaction temperature to ۱۱۰۰ ˚C, the particle size scale was in micrometre range. Ultraviolet–visible spectra analysis showed that the nanostructured Y۲Ce۲O۷ powder (S۲) possessed strong light absorption property in the ultraviolet light region. The direct optical band gap was calculated as ۳.۱۵ eV. Besides, the photoluminescence spectrum for the obtained material (S۲) was investigated at λex=۲۳۰ nm as excitation wavelength. It showed a strong emission peak at ۴۲۵ nm. Catalytic performance of the synthesized nanomaterial (S۲) was also investigated in alcohol oxidation reactions which showed excellent efficiency as ۷۵%.
کلیدواژه ها:
نویسندگان
Nadali Ramezani
Department of Chemistry, Science and Research Branch, Islamic Azad University, Tehran, Iran.
Morteza Enhessari
Department of Chemistry, Naragh Branch, Islamic Azad University, Naragh, Iran.
Mohammad Yousefi
Department of Chemistry, Science and Research Branch, Islamic Azad University, Tehran, Iran.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :