Effects of fusion plasma ions on Aluminum and Tungsten samples using a plasma focus device: a comparison study
محل انتشار: فصلنامه فیزیک و مهندسی پرتو، دوره: 4، شماره: 1
سال انتشار: 1402
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 135
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_RPE-4-1_002
تاریخ نمایه سازی: 26 دی 1401
چکیده مقاله:
In this research, the effect of ions produced in deuterium plasma on Tungsten (W) and Aluminum (Al) plates has been investigated using a plasma focus device with the specifications of (C=۱۰.۴ μF, V=۲۳ kV, E=۲.۷۵ kJ). The W samples used because it is one of the key elements in the Tokamak device. Because we wanted to put the W samples at the distance from the anode top with maximum plasma produced ions, we should find the optimum place. Due to the high cost of W samples, we used Al samples to find the optimal conditions. The samples were irradiated at ۸ cm distance from the anode top with deuterium ions produced by a plasma focus device. The sample analyses were done by the SEM and EDX methods. The sample irradiation by deuterium plasma ions caused a lot of damages and bubble formation on the sample surfaces. The analyses showed the extent of surface damage and the number of ions deposited on the surface. The number of damages on the Al surface was much higher than W. Bubbles were formed on the surface were due to the impact of deuterium ions on the W and Al samples. Also, the deuterium ion energy was measured with a Faraday cup as about ۵۰ keV.
کلیدواژه ها:
نویسندگان
Ali Adeli Ahmadabadi
Radiation Application Department, Faculty of Nuclear Engineering, Shahid Beheshti University, Tehran, Iran
Zahra Shahbazi rad
Radiation Application Department, Faculty of Nuclear Engineering, Shahid Beheshti University, Tehran, Iran
Fereidon Abbasi Davani
Radiation Application Department, Faculty of Nuclear Engineering, Shahid Beheshti University, Tehran, Iran
Behjat Ghasemi
Radiation Application Department, Faculty of Nuclear Engineering, Shahid Beheshti University, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :