Effect of Ply Orientation on Residual Stresses and Their Influence on Mode I Fracture Toughness of Glass-Epoxy Composites with ۰°//۰° Crack Interface
محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 18، شماره: 4
سال انتشار: 1400
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 113
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMSEI-18-4_003
تاریخ نمایه سازی: 24 بهمن 1401
چکیده مقاله:
The energy release rate for delamination in a laminated composite is supposed to be the material property being considered as independent of non-material property variables. However, Mode I fracture toughness(GI) is found to vary with lamina arrangement, geometrical dimensions, and process-induced stresses. In this investigation, the influence of lamina stacking arrangement on process-induced stresses and their effects on GI of laminated composites are studied. Unidirectional (UD) ([۰]۱۶) and cross-ply ([۹۰۲/۰۶]s, [۹۰۴/۰۴]s and [۹۰۶/۰۲]s) Glass/ epoxy (GE) composites with the delamination plane at ۰◦//۰◦ were prepared by manual layup method and post-cured at ۱۲۰ °C for ۴ hours. GI of composite laminates were experimentally determined using a double cantilever beam(DCB) specimen as per ASTM D ۵۵۲۸. The slitting method was applied to determine the Process-induced stresses in GE laminates. The stacking sequence of laminas was found to have a noticeable effect on the state of residual stresses and GI of GE laminates. Residual stresses do not have much influence on the GI for delamination initiation, whereas GI for the crack propagation was found to increase with a gradual increase in compressive residual stresses in GE laminates.
کلیدواژه ها:
نویسندگان
Umarfarooq Maktedar Abdulkhadar
SDM College of Engineering & Technology, Dharwad
Patil Somalingana Shivakumar Gouda
SDM College of Engineering & Technology, Dharwad
Anil Shirahatti
Jain College of Engineering, Belagavi
Gonal Basavaraja Veeresh Kumar
National Institute of Technology, Tadepalligudem, Andhra Pradesh,
Nagaraj Ramalingyya Banapurmath
B.V.B. College of Engineering and Technology, KLE Technological University,
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :