The Effect of Temperature on the Purity of Nano-Scale Tantalum Powder Produced from Its Scrap by Reaction with Magnesium and Calcium
محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 18، شماره: 2
سال انتشار: 1400
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 95
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMSEI-18-2_004
تاریخ نمایه سازی: 24 بهمن 1401
چکیده مقاله:
In this study, Ta powder was produced from Ta scarp via chemical processes using Mg and Ca powders. At first, Tantalum scraps were converted to Tantalum oxide (Ta۲O۵) at ۱۱۰۰˚C in an oxygen atmosphere. Tantalum oxide was reduced to Tantalum powder with Mg in a vacuum environment at ۹۵۰ to ۱۲۰۰˚C for ۳ hours. The obtained Ta powders further were reacted with Ca at ۹۵۰˚C for ۵ hours in a vacuum atmosphere. The powders were analyzed through X-ray diffraction patterns (XRD), scanning electron microscopy (SEM), as well as oxygen measurement. The results show that the average particles size of the produced Ta powders is about ۵۸ nm with oxygen contents of ۲۵۰ ppm.
کلیدواژه ها:
نویسندگان
Gholam Hussein Borhani
Dept. of Materials Eng., Malek-ashtar University of Tech.
Saeed Reza Bakhshi
Dept. of Materials Eng., Malek-ashtar University of Tech.
Sadegh Soltani
Dept. of Materials Eng., Malek-ashtar University of Tech.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :