Optimization of Solvent Extraction Parameters for Separation of Samarium and Lutetium from Acidic Media Using Response Surface Methodology (RSM)
محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 18، شماره: 1
سال انتشار: 1399
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 104
فایل این مقاله در 13 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMSEI-18-1_006
تاریخ نمایه سازی: 24 بهمن 1401
چکیده مقاله:
Separation of samarium and lutetium was investigated through solvent extraction from their mixed aqueous species using commercial extractants of D۲EHPA and PC۸۸A. The Response Surface Method (RSM) was utilized to design the solvent extraction experiments. In which, a Central Composite Design (CCD) was applied to set the optimum conditions for highest separation factors between Sm and Lu. Design of Experiments (DOE) was conducted by making use of four operating variables, namely initial pH of the aqueous solutions (A: ۰.۲–۲.۶), extractant concentration (B: ۰.۰۱-۰.۰۹ molar), mole fraction of D۲EHPA in the extractant mixture (C: ۰ - ۰.۸) and a type of acidic solution (D: sulfuric and nitric acid) at three levels. The results indicated that the initial pH was the most paramount variable in solvent extraction of samarium and lutetium, while in the case of lutetium, the molar fraction of D۲EHPA in the mixed extractants was non-influential. The statistical model predictions were confirmed by experiments for both samarium and lutetium extraction with high validity parameter of ۹۷ and ۹۸%, respectively. The optimum conditions for samarium and lutetium separation were identified as: A=۰.۸, B= ۰.۰۵, C= ۰.۲ and D= sulfuric acid. According to the findings of the model, the desirability value at the optimum conditions was evaluated as about ۰.۹۳, in which ۷۱% of lutetium was extracted while the amount of extracted samarium was only less than ۱%.
کلیدواژه ها:
نویسندگان
Hamed Tavakoli
Iran University Science and Technology
Mohammad Reza Aboutalebi
Iran University of Science and Technology
Seyed Hosein Seyedein
Iran University of Science and Technology
Seyed Nezameddin Ashrafizadeh
Iran University of Science and Technology
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :