Impact of Carbon Nanotubes Reinforcement on Microstructural and Tribological Characteristics of Air Plasma Sprayed Conventional Alumina-Titania (Al۲O۳-۳wt%TiO۲) Coatings
محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 17، شماره: 3
سال انتشار: 1399
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 121
فایل این مقاله در 12 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMSEI-17-3_011
تاریخ نمایه سازی: 1 اسفند 1401
چکیده مقاله:
The microstructural characteristics, mechanical properties, and wear characterization of air plasma sprayed coatings obtained from Carbon nanotubes (CNTs) reinforced Al۲O۳-۳wt%TiO۲ powders were examined at different loading conditions and different percentage proportion of CNTs. The CNTs in the proportion of ۲, ۴, and ۶wt% were used as nanofillers to modify the properties of coatings. The uniform dispersion of CNTs throughout the powder particles can be observed from the SEM micrographs. The porosity of the microstructure of the coatings was measured by image analysis. Also, the mechanical properties such as microhardness and surface roughness were measured by microhardness tester and profilometer, respectively. The wear tribometer was used to analyze the tribology of the coatings by varying different parameters. The different loading conditions used were low load (۰.۵ kgf), moderate load (۱.۰ kgf), and elevated load (۱.۵kgf), respectively. The microhardness showed a slight increase with an increase in the percentage of CNTs proportion. Similarly, the surface roughness value showed a decreasing trend, since the CNTs were filled in the pores. From wear tests, it was observed that the coefficient of friction and wear rate were very less at ۶wt% CNTs and ۱.۵kgf load. This was mainly due to the bridging of CNTs in between the splats. This implies that CNTs were one of the most suitable additives for improving the microstructural and tribological characterization of the ceramic coatings.
کلیدواژه ها:
نویسندگان
M. T. Basha G
Vellore Institute of Technology, Vellore-۶۳۲۰۱۴, Tamilnadu, India
V. Bolleddu
Vellore Institute of Technology, Vellore-۶۳۲۰۱۴, Tamilnadu, India
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :