Significant Increase in Strength and Elongation of Al-۳.۷ Cu-۱Mg Alloy Via Short Age Treatment Cycle
محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 17، شماره: 3
سال انتشار: 1399
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 132
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMSEI-17-3_004
تاریخ نمایه سازی: 1 اسفند 1401
چکیده مقاله:
In this paper, the effect of two-step precipitation hardening on the mechanical properties of Al-۳.۷Cu-۱Mg was investigated. For this meaning, some specimens were subjected to the first step aging at ۱۷۵, ۱۹۰ and ۲۰۵°C for ۲ h, once the samples solution treated at ۵۰۰°C. To have stable precipitates uniformly distributed in the microstructure and to reduce the heat treatment time, the second step was implied at ۶۵°C. The tensile and hardness tests were performed at ambient temperature immediately after aging. The results indicated that depending on the first step temperature, the second aging time affects the alloy mechanical behavior in different aspects. A factor named SNMP introduced to determine the cycle giving the best mechanical properties. The strength and elongation increase ۱.۵ and ۲ times respectively; compared to the values reported in the DIN EN ۷۵۵-۲ standard by performing the two-step aging cycle, consisting of the first-stage at ۱۷۵°C and the second step at ۶۵°C for ۱۰ hours. Moreover, using the proposed two-step aging, the heat treatment time was reduced considerably compared to the conventional precipitation hardening process.
کلیدواژه ها:
نویسندگان
B. Mirzakhani
Department of Materials Science and Engineering, Faculty of Engineering, Arak University, Arak ۳۸۱۵۶-۸-۸۳۴۹, Iran.
Y. Payandeh
Department of Materials Science and Engineering, Faculty of Engineering, Arak University, Arak ۳۸۱۵۶-۸-۸۳۴۹, Iran.
H. Talebi
Department of Materials Science and Engineering, Faculty of Engineering, Arak University, Arak ۳۸۱۵۶-۸-۸۳۴۹, Iran.
M. Maleki
Department of Materials Science and Engineering, Faculty of Engineering, Arak University, Arak ۳۸۱۵۶-۸-۸۳۴۹, Iran.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :