Hot Deformation of the Mn-Ni-Cr Alloy During Compression
محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 17، شماره: 1
سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 199
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMSEI-17-1_010
تاریخ نمایه سازی: 1 اسفند 1401
چکیده مقاله:
In this paper a constitutive equation was considered for the isothermal hot compression test of the Mn-Ni-Cr alloy. The hot compression test was performed in the strain rate range of ۰.۰۰۱-۰.۱ s-۱ and deformation temperature was varied from ۷۰۰ to ۹۰۰ °C. A considerable reduction in flow stress was observed regardless of the strain rate when temperature was increased from ۷۰۰ to ۷۵۰ °C. DTA and XRD evaluation revealed that the removal of Mn۳Cr phase and formation of the single solid solution phase were the reason for the flow stress reduction. At the low deformation temperature (۷۰۰°C) and the high strain rate (۰.۱ s-۱), a partially recrystallized microstructure was observed; this was such that with increasing the temperature and decreasing the strain rate, a recrystallized microstructure was completed. Also, the relationships between flow stress, strain rate and deformation temperature were addressed by the Zener-Holloman parameter in the exponent type with the hot deformation activation energy of ۳۰۱.۰۷ KJ/mol. Finally, the constitutive equation was proposed for predicting the flow stress at various strain rates and temperatures.
کلیدواژه ها:
نویسندگان
M. Sadeghi
Materials Engineering Department, Malek Ashtar University of Technology, Shahin Shahr, Iran
M. Hadi
Department of Materials Science and Engineering, Golpayegan University of Technology, Golpayegan, Iran
O. Bayat
Department of Materials science and Engineering, Hamedan University of Technology, Hamedan, Iran
H. Karimi
Materials Engineering Department, Malek Ashtar University of Technology, Shahin Shahr, Iran.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :