Effect OF SI and AL on the Microstructure, Mechanical Properties and Machinability of ۶۵CU-۳۵ZN Brass

محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 16، شماره: 2
سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 88

فایل این مقاله در 12 صفحه با فرمت PDF قابل دریافت می باشد

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این مقاله:
https://civilica.com/doc/1606497

شناسه ملی سند علمی:

JR_IJMSEI-16-2_003

تاریخ نمایه سازی: 1 اسفند 1401

چکیده مقاله:

Relations between the microstructure, mechanical properties and machinability of as-cast ۶۵Cu-۳۵Zn brass with various amounts of Al from ۰ to ۴.۷۲ and Si from ۰ to ۳.۶۲ wt% were investigated. Both Si and Al initially enhanced the UTS and toughness of the brass samples, which led to improvement in machinability due to a reduction in the main cutting force. A duplex brass with random oriented α plates in β’ matrix was found to have the best machinability among the other microstructures. It was found that beside the presence of brittle phases, such as β’ phase in the microstructure, the morphology and hardness of the phases involved had significant influence on machinability.

کلیدواژه ها:

Brass ، Silicon ، Aluminum ، microstructure ، machinability

نویسندگان

M. Adineh

Shahid Bahonar University of Kerman

H. Doostmohammadi

Shahid Bahonar University of Kerman

R. Raiszadeh

Shahid Bahonar University of Kerman

مراجع و منابع این مقاله:

لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :
  • Lee, D. B. and Moon, J. J., The effect of ...
  • Mohammadnejad, M., Ehteshamzadeh, M. and Soroushian, S., Effect of annealing ...
  • Pugacheva, N. B., Pankratov, A. A., Frolova, N. Y. and ...
  • Asanovi, V., Deliji, K. and Jaukovi, N., Isothermal decomposition of ...
  • Chen, B., Liang, C., Fu, D. and Ren, D., Corrosion ...
  • Fricoteaux, P. and Rousse, C., Nanowires of Cu–Zn and Cu–Zn–Al ...
  • García, P., Rivera, S., Palacios, M. and Belzunce, J., Comparative ...
  • Schultheiss, F., Johansson, D., Linde, M., Tam, P. L., Bushlya, ...
  • Schultheiss, F., Johansson, D., Bushlya, V., Zhou, J., Nilsson, K. ...
  • Nobel, C., Klocke, F., Lung, D. and Wolf, S., Machinability ...
  • Doostmohammadi, H. and Moridshahi, H., Effects of Si on the ...
  • Toulfatzis, A. I., Pantazopoulos, G. A. and Paipetis, A. S., ...
  • Alirezaei, M. and Doostmohammadi, H., Microstructure evolution in cast and ...
  • Rajabi, Z. and Doostmohammadi, H., Effect of Addition of Tin ...
  • Vilarinho, C., Davim, J. P., Soares, D., Castro, F. and ...
  • Ånmark, N., Karasev, A. and Jönsson, P. G., The effect ...
  • ASTM E۸ / E۸M-۱۱, Standard test methods for tension testing ...
  • Davis, J. R., ASM Specialty Handbook: Copper and Copper Alloys, ...
  • Wang, J., Xu, H., Shang, S., Zhang, L., Du, Y., ...
  • Hsieh, C. C., Wang, J. S., Wu, P. T. Y. ...
  • Li, J., Guo, H. and Zhou, P., Experimental study and ...
  • Williams, J. A., Deformation diagrams of chip forming mechanisms. J. ...
  • Hofmann, U. and El-Magd, E., Behaviour of Cu-Zn alloys in ...
  • Sabih, A. and Nemes, J. A., Internal ductile failure mechanisms ...
  • Dørum, C., Hopperstad, O. S., Berstad, T. and Dispinar, D., ...
  • Komanduri, R. and Brown, R. H., On the mechanics of ...
  • Morehead, M. D., Huang, Y. and Luo, J., Chip morphology ...
  • Liu, Y., Research of the formation mechanism of widmanstätten ferrite ...
  • Gil, F. J., Ginebra, M. P., Manero, J. M. and ...
  • Yang, Y., Li, X. M., Tong, X. L., Zhang, Q. ...
  • Pantazopoulos, G. A. and Toulfatzis, A. I., Fracture modes and ...
    • نمایش کامل مراجع