The Simulation of Texture of Al۰.۳CoCrFeNi High Entropy Alloy after Cold Deformation using Visco-Plastic Self-Consistent Model
محل انتشار: مجله شکل دهی مواد، دوره: 10، شماره: 1
سال انتشار: 1402
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 88
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMF-10-1_006
تاریخ نمایه سازی: 28 خرداد 1402
چکیده مقاله:
In the present study, a visco-plastic self-consistent model (VPSC) was used to predict the Al۰.۳CoCrFeNi texture after cold rolling. The alloy under examination was produced via vacuum arc remelting and casting (VAR casting). Then, it was remelted four times to have the best structure homogeneity. However, the produced ingot was then homogenized at ۱۰۵۰°C for ۱۰ h to remove the residual stress and reduce the micro-macro-segregation. This was followed by ۷۵% cold reduction which was employed in seven passes. In order to simulate the Al۰.۳CoCrFeNi texture via the VPSC model, affine schemes and hardening parameters were used in this model. Moreover, this model was performed by Fortran ۷۷ programming languages, and grain fragmentation and co-rotational effect were used in this code. In this study, a simulation process was used for ۳۰۰ and ۱۰۰۰ grains. After that, simulation results were compared with experimental textures that were measured by the X-ray diffraction method. The results showed that both experimental and simulated textures have an acceptable compatibility. However, there are differences between the measured and simulated results, which can be attributed to the number of grains of estimated and simulated cases.
کلیدواژه ها:
نویسندگان
A.H. Hosseinifar
Department of Materials and Metallurgical Engineering, Amirkabir University of Technology (Tehran Polytechnic), Tehran, Iran
K. Dehghani
Department of Materials and Metallurgical Engineering, Amirkabir University of Technology (Tehran Polytechnic), Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :