Green Synthesis of Au-doped SnO۲ Nanoparticles Using Teucrium Polium Plant Extract for the Evaluation of Their Physicochemical and Antibacterial Properties
محل انتشار: مجله علوم پیشرفته زیست پزشکی، دوره: 13، شماره: 2
سال انتشار: 1402
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 100
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JABS-13-2_007
تاریخ نمایه سازی: 31 تیر 1402
چکیده مقاله:
Background & Objective: The biological production of nanoparticles (NPs) is a technique that has garnered a lot of interest because it is inexpensive, straightforward, and friendly to the natural environment. This study explores the green synthesis of Au-doped SnO۲ NPs using Teucrium polium plant extract and evaluates their antimicrobial properties in comparison with two commonly used antibiotics.
Materials & Methods: Initially, an extract of Teucrium polium was made using water, and then it was combined with solutions of tin (II) chloride dehydrate [SnCl۲.۲H۲O] and gold (III) chloride trihydrate [HAuCl۴.۳H۲O]. The crystal structure was studied using X-ray diffraction (XRD). The form, structure, and grain size of the NPs were analyzed using scanning electron microscope (SEM) and transmission electron microscope (TEM). The synthesized NPs were tested for their antibacterial properties.
Results: The XRD and EDS analyses revealed that the SnO۲:Au phase formed an average crystallite size of ۲۲ nm and an Au dopant content of around ۲%. The SEM and TEM investigations demonstrated that the NPs were formed in a regular and nanoscale manner, with diameters ranging from ۲۵ to ۳۰ nm. MIC and MBC of SnO۲: Au NPs against the studied bacteria(S.aureus ATCC ۴۳۳۰۰, P.aeruginosa PAO۱) were reported ۹.۶±۰.۱۳- ۹.۶±۰.۰۷ μg/mL and ۲۵.۹±۱۱.۵- ۳۲.۵±۱۱.۲ μg/mL
Conclusion: Green-synthesized NPs exhibit significant antimicrobial activity against both Gram-positive and Gram-negative bacteria, even at low concentrations. The NPs effectively eliminate bacteria and prevent biofilm formation.
کلیدواژه ها:
نویسندگان
مرات کریمی
Institute of Nanoscience and Nanotechnology, University of Kashan, Kashan, Iran
احسان صادقی
Institute of Nanoscience and Nanotechnology, University of Kashan, Kashan, Iran
مصطفی زاهدی فر
Institute of Nanoscience and Nanotechnology, University of Kashan, Kashan, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :