Evaluation of Microleakage and Biocompatibility of Universal Adhesive Containing Titanium Dioxide Nanoparticles: A Comparative In Vitro Study
محل انتشار: مجله علوم پیشرفته زیست پزشکی، دوره: 11، شماره: 4
سال انتشار: 1400
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 104
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JABS-11-4_004
تاریخ نمایه سازی: 31 تیر 1402
چکیده مقاله:
Background & Objective: Although dental composites have undergone a high level of development in recent years, there are still difficulties including microleakage. The incorporation of nanoparticles (NPs) in dental materials can produce antibacterial effects, but the effect of TiO۲ NPs on microleakage has not yet been investigated. The present study aimed to determine the effect of TiO۲ NPs incorporation in the universal single bond and pretreatment with them on microleakage of clV cavities using both total-etch and self-etch approaches.
Materials & Methods: Standard clV cavities were prepared on the buccal surfaces of the sixty non-carious human molar teeth. The restoration of samples was carried out with ۶ different methods and randomly divided into six groups of ten subjects. Microleakage in both gingival and occlusal margins was determined after placement in ۲% basic fuschin solution for ۲۴h. Biocompatibility of a universal single bond was evaluated by MTT assay.
Results: In both occlusal and gingival margins in all groups, the application of TiO۲ NPs was better than no application. We observed the relatively low cytotoxic effect of TiO۲ NPs incorporated in the universal adhesive on NIH-۳T۳ cell viability.
Conclusion: Regarding the limitations of the present investigation, using TiO۲ NPs with both total-etch and self-etch approaches to universal single bond may lead to a decrease in the microleakage of resin composite restorations.
کلیدواژه ها:
نویسندگان
فاطمه کوهپیما
Department of Operative Dentistry, Biomaterial Research Center, Faculty of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran
محمدجواد مختاری
Department of Biology, Zarghan Branch, Islamic Azad University, Zarghan, Iran
مرضیه سالاری
Department of Operative Dentistry, Biomaterial Research Center, Faculty of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :