ON THE REACTIONS IN ILMENITE, ALUMINUM AND GRAPHITE SYSTEM
محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 13، شماره: 1
سال انتشار: 1394
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 82
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMSEI-13-1_009
تاریخ نمایه سازی: 26 مرداد 1402
چکیده مقاله:
Al۲O۳/TiC composites are used as cutting tools for machining gray cast iron and steels. The addition of iron improves the toughness of Al۲O۳/TiC composites. Ilmenite, aluminum and graphite can be used to produce in-situ Al۲O۳/TiC–Fe composites. However, the formation mechanism and reaction sequences of this system are not clear enough. Therefore, the present research is designed to determine the reactions mechanism of the first step of reactions that may be occurred between raw materials. In this research, pure ilmenite was synthesized to eliminate the effects of impurities available in the natural ilmenite in the system. The milled and pressed samples, prepared from the synthesized ilmenite, aluminum and graphite mixture with a molar ratio of ۱:۲:۱, were heat treated at ۷۲۰°C for ۴۸h. In addition, two samples one containing ilmenite and aluminum with a molar ratio of ۱:۲ and ilmenite and graphite with a molar ratio of ۱:۱ were heat treated at ۷۲۰°C for ۴۸h. The final products were analyzed with XRD. It was found that at ۷۲۰°C, aluminum reacts with FeTiO۳, forming Fe, TiO۲ and Al۲O۳. Since the aluminum content used in the mixture was more than the stoichiometry for reaction of ilmenite and aluminum, some unreacted aluminum remains. Therefore, the residual aluminum reacts with the reduced Fe to form Fe۲Al۵.
کلیدواژه ها:
نویسندگان
R. Khoshhal
Birjand University of Technology,Birjand
M. Soltanieh
Department of Materials Science and Engineering,Iran University of Science and technology,
M. A. Boutorabi
Department of Materials Science and Engineering,Iran University of Science and technology,
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :