Growth Defects and Chromium Content Loss during the Deposition of Stainless Steel by CAE-PVD and Its Effect on the Corrosion and Passivation Behavior of the Coating
سال انتشار: 1394
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 55
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ISSIRAN-12-2_002
تاریخ نمایه سازی: 5 شهریور 1402
چکیده مقاله:
In the present study, the effects of growth defects and chromium content loss on the degradation of corrosion and passivation of cathodic arc evaporation (CAE-PVD) of stainless steel coating were investigated in ۲ M sulphuric acid solution. EDS analysis indicated that the micro-particles were obtained during the coating growth. In addition, it was detected that the growth defects had poor adhesion to the coating matrix and in the open circuit potential (OCP), they were detached from the coating, providing appropriate conditions for the penetration of the solution. In addition, loss of chromium during evaporation was found to be detrimental to the passivation of the stainless steel coating and the formation of a porous oxide layer. The average percent of the main elements of the coating, according to EDS area analysis, was Fe-۱۳Cr-۶Ni. Moreover, the lower semicircle diameter of the coating in electrochemical impedance spectroscopy (EIS) measurements revealed the lower polarization resistance of it, in comparison to that of the bulk ۳۰۴ stainless steel.
کلیدواژه ها:
نویسندگان
A. Sanati
Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶- ۸۳۱۱۱, Iran.
K. Raeissi
Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶- ۸۳۱۱۱, Iran.
H. Edris
Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶- ۸۳۱۱۱, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :