Preparation, Identification, and Evaluation of the Thermal Properties of Novolac Resins Modified with TiO۲, MgO, and V۲O۵ Oxides
سال انتشار: 1403
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 62
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_MACS-11-1_001
تاریخ نمایه سازی: 3 آبان 1402
چکیده مقاله:
It is essential to improve thermal insulation. In this study, titanium dioxide (TiO۲), magnesium oxide (MgO), and vanadium pentoxide (V۲O۵) were used as additives to modify phenolic novolac resin by the solution mixing method. Different weight percentages of resin nanoparticles (NPs) were added, and nanocomposites with different weight percentages were prepared. These nanocomposites were investigated by field emission scanning electron microscope (FE-SEM), X-ray diffraction spectroscopy (XRD), and oxyacetylene flame test (OFT). The FE-SEM images showed that the NPs were dispersed on the surface of the novolac resin at low concentrations. However, at high concentrations, the dispersion was suppressed in some cases by aggregation in the nanocomposites. The OFT test proved that by increasing the content of NPs in the nanocomposite, the back surface temperature of the sample decreased, thus improving the thermal insulation properties.
کلیدواژه ها:
نویسندگان
Mohsen Rezaei Qazviniha
Department of Chemistry, Faculty of Sciences, Zanjan University, Zanjan, Iran
Farideh Piri
Department of Chemistry, Faculty of Sciences, Zanjan University, Zanjan, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :