A Study on the Mechanical Properties of Dual Phase Steels Prepared by the Direct and Step Quenching Procedure
سال انتشار: 1393
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 66
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ISSIRAN-11-2_006
تاریخ نمایه سازی: 6 آبان 1402
چکیده مقاله:
Two different dual phase steels were prepared from low carbon manganese steel after the elimination of the banding using the direct quenching (DQ) and the step quenching (SQ) procedures. Different heat treatments resulted in different martensite morphologies, microstructures and mechanical properties. The heat treatments were designed in such a way to obtain a ۰.۲۵ volume fraction of martensite (Vm). For this reason, an intercritical temperature of ۷۲۵ oC was applied. Furthermore, the tensile and impact properties were discussed. The results from the impact and tensile tests at different temperatures showed that the ductile-brittle transition temperatures for the DQ and SQ treatments were -۴۹ and -۶ oC respectively, while the DQ had better toughness.
کلیدواژه ها:
نویسندگان
T. Dallali Isfahani
Department of Materials Science and Engineering, Golpayegan University of Technology, Golpayegan, Iran
H. Sharifi
Faculty of Engineering, Shahrekord University, Shahrekord, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :