The Effect of the Carbon Nanotube Content on the Corrosion Behaviour of Ni-P-CNT Composite Coating
سال انتشار: 1391
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 55
فایل این مقاله در 5 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ISSIRAN-9-1_001
تاریخ نمایه سازی: 6 آبان 1402
چکیده مقاله:
In the present study, Ni-P-CNT composite coating was successfully fabricated via electroless plating. Scanning electron microscopy (SEM) was used to characterize the coatings. The effect of CNTs concentration in the bath on its content in the composite coatings was studied. Furthermore, the corrosion behaviour of the coatings with different contents of CNTs was evaluated using Tafel polarization and electrochemical impedance spectroscopy (EIS) methods in ۳.۵ wt.% NaCl aqueous solution at the room temperature. The results showed that the corrosion resistance of the Ni–P-CNT composite coatings was excellent in comparison with that of the Ni-P coatings and the content of incorporated CNTs played a key role in the passivation and corrosion resistance.
کلیدواژه ها:
نویسندگان
M. Alishahi
Department of Mining and Metallurgical Engineering, Amirkabir University of Technology, Tehran, Iran
S. Monirvaghefi
Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran
A. Saatchi
Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :