An Investigation of Casting Defects Revealed in Forming Process of USD۷ Steel
سال انتشار: 1385
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 86
فایل این مقاله در 5 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ISSIRAN-3-2_005
تاریخ نمایه سازی: 6 آبان 1402
چکیده مقاله:
USD۷ is one of the steel products of Isfahan Steel Company. It is cast in continuous casting moulds and rolled up to a rod of ۵ mm diameter. Finally, it is wire drawn up to ۳ mm and used as welding electrodes. This steel contains ۰.۰۵ to ۰.۰۹ wt. % carbon. The acceptable limit of the aluminium in this class of steel is less than ۰.۰۰۳ wt%. Therefore, it is categorized as rimmed steel. During forming process, there are some defects such as tearing and laminating that stop the forming process. The aim of this research is to evaluate the factors causing the aforementioned defects. It was found that there were many porosities in the cast ingot. The area around these porosities was analyzed with EDS method, and inclusions with MnO and (Fe, Mn)O chemical composition were observed. It was found that they were external inclusions (slag inclusions caused by reoxidation and entrapment phenomena). Because of the presence of these inclusions, these porosities are not welded together during rolling process. Therefore, in the next steps of the forming process, these defects are revealed.
کلیدواژه ها:
نویسندگان
A. Homayoun
Department of Materials and Metallurgical Engineering, Iran University of Science & Technology, Tehran, ۱۶۸۴۴, Iran
M. Shahmohammadi
Department of Materials and Metallurgical Engineering, Iran University of Science & Technology, Tehran, ۱۶۸۴۴, Iran
M. Soltanieh
Department of Materials and Metallurgical Engineering, Iran University of Science & Technology, Tehran, ۱۶۸۴۴, Iran
A. Afzali
Isfahan Steel Company, Isfahan, ۸۴۹۳۱, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :