چکیده مقاله:
In this survey, composite parts of Alumina-zirconia was produced by gel-casting method and the impact of differentparameters such as composition of polymeric materials and sintering temperature on strength and microstructure of the final products is investigated. The results showed that increase in green strength of gel-casting samples obtained by the polymerization rate. Furthermore, increase of Cross-linker in the monomer fixed led to the increase in green strength of the produced parts. Bending strength and relative density measurements of the samples showed the highest bending strength and relative density achieved at sintering temperature of 1500oC.
کلیدواژه ها:
نویسندگان
Reza bahaadinbeigiand
Department of Metallurgy and Materials Science, Faculty of Engineering, ShahidBahonar University of Kerman
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :