Laser Scanning Speed Influences on Assessment of Laser Remelted Commercially Pure Titanium Grade ۲
محل انتشار: ماهنامه بین المللی مهندسی، دوره: 37، شماره: 1
سال انتشار: 1403
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 49
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJE-37-1_016
تاریخ نمایه سازی: 15 آذر 1402
چکیده مقاله:
In this research, the influences of laser surface remelting using different scanning speeds on the microstructure, roughness, and hardness of Commercial pure Titanium (Grade ۲) were investigated. High power Nd: YAG pulsed laser was used. The laser scanning speeds used in this study were ۴, ۶, ۸, and ۱۰ mm/s and the other laser parameters (power, pulse frequency, beam diameter) were constant. The corrosion performance of the laser surface remelted and Cp titanium was then evaluated by potential dynamic measurements in a ۳.۵% NaCl solution. The results revealed that due to the diffusionless transformation after laser surface treatment and the formation of the martensite phase, the surface post-laser treatment was significantly different from those before the treatment. The results were indicated using an optical microscope, FE-SEM, XRD, AFM, and microhardness analysis. It was found the lowest scanning speed, ۴ mm/s, had the slightest roughness and the smallest average grain size (۲۶.۰۶ nm) due to the high input energy and slow cooling rate, while the highest scanning speed (۱۰ mm/s) had the greatest microhardness (۲۹۱.۵ Hv) due to the short interaction time between the substrate surface and laser beam and the higher cooling rate. The results also demonstrated the obvious improvement in the pitting resistance of Cp Ti in harsh environments as a result of the influence of laser remelting.
کلیدواژه ها:
نویسندگان
T. Mohammed Naji
Department of Production Engineering and Metallurgy, University of Technology, Baghdad, Iraq
M. A. Ali Bash
Department of Production Engineering and Metallurgy, University of Technology, Baghdad, Iraq
A. M. Resen
Department of Production Engineering and Metallurgy, University of Technology, Baghdad, Iraq
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :