Effects of ZSM-۵ Preparation Conditions on Textural Properties and Catalytic Cracking of n-Hexane
محل انتشار: مجله علوم و فن آوری نفت، دوره: 9، شماره: 4
سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 56
فایل این مقاله در 14 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JPSTR-9-4_005
تاریخ نمایه سازی: 29 آذر 1402
چکیده مقاله:
In this study, the effects of crystallization temperature, crystallization time, and pH value on the textural properties of synthetic ZSM-۵ were investigated by the orthogonal test method. Furthermore, the effects of ZSM-۵ catalysts synthesized under different preparation conditions on their reactivity during catalytic cracking were evaluated. Moreover, the results have shown that the three factors that affect the ZSM-۵ synthesis are in the following order: crystallization temperature > crystallization time > pH value. In addition, the optimal conditions for synthesizing ZSM-۵ catalysts were crystallization temperature of ۱۷۰ °C, crystallization time of ۴۸ h, and pH of ۱۱. Furthermore, under these conditions, the specific surface area, pore-volume, and acidity of the synthetic zeolite were moderate, and the hydrothermal stability was ideal. Finally, when the optimal conditions were applied to the catalytic cleavage of n-hexane, the synthesized zeolite exhibited good activity and stability.
کلیدواژه ها:
نویسندگان
Sheng-tao Qu
School of Environmental and Chemical Engineering, Liaoning Shihua University, Fushun, China
Dong-mei Liu
School of Environmental and Chemical Engineering, Liaoning Shihua University, Fushun, China
Xin Shi
School of Environmental and Chemical Engineering, Liaoning Shihua University, Fushun, China
Hai-yan Wang
School of Environmental and Chemical Engineering, Liaoning Shihua University, Fushun, China
Xin Wang
China National Petroleum Corporation Fushun Petrochemical Company Detergent Chemical Plant, Fushun, China
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :