Investigation of hydrothermal process time on the size of carbon micro- and nano-spheres
سال انتشار: 1396
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 47
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JOPN-2-2_006
تاریخ نمایه سازی: 25 بهمن 1402
چکیده مقاله:
In this study, carbon nano-micro spheres with tightly controllable size, regularand perfect shape, high yields and narrow size distribution were prepared simply fromglucose and DI water as precursors using a hydrothermal method. By setting the initialconcentration of glucose solution and changing the hydrothermal process time at aconstant temperature of ۱۶۰ °C, carbon spheres with various sizes were synthesized in asealed autoclave. The relationship between the average carbon sphere size andhydrothermal process time has been discussed. By increasing the hydrothermal process timeat a constant temperature (۱۶۰ ° C) and a constant concentration of glucose solution (۰.۷۵ molar),carbon nano-micro spheres were obtained. The diameters of carbon nano-micro spheressynthesized in this study ranged from ۹۰ nm to ۴.۵ μm. The obtained carbon nano-microspheres were analyzed by different techniques including scanning electron microscopy(SEM), X-ray diffraction patterns (XRD), energy dispersive spectrometry (EDS) andRaman analysis. In addition, the existence of surface functional groups on carbonnano/micro spheres was characterized by Fourier transform infrared (FTIR)measurements.
کلیدواژه ها:
نویسندگان
Khadijeh Hemmati Kahradeh
Department of Physics, Faculty of Basic Science, Tarbiat Modares University, Tehran, Iran.
Esmaiel Saievar-Iranizad
Department of Physics, Faculty of Basic Science, Tarbiat Modares University, Tehran, Iran.
Amir Bayat
Department of Physics, Faculty of Basic Science, Tarbiat Modares University, Tehran, Iran.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :