ZrO۲ Nanoparticles: Optical Properties of Tetragonal Phase and Enhanced Photocatalytic Activity
سال انتشار: 1399
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 57
فایل این مقاله در 12 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JOPN-5-2_002
تاریخ نمایه سازی: 25 بهمن 1402
چکیده مقاله:
Tetragonal zirconia (t-ZrO۲) nanoparticles were synthesized from thezirconium chloride using the co-precipitation technique and characterized by variousmeasurement techniques. FESEM analysis further revealed spherical shaped NPs andHR-TEM analysis determined the size of the particles in the range of ۱۴.۵ nm. The bandgap energy was estimated ۴.۰ eV. The UV (۳۵۰ nm) emission was observed from PLspectrum. The photocatalytic degradation of the as-prepared ZrO۲ nanoparticles werestudied under UV light irradiation using ciprofloxacin (CIP) as a model organicpollutant. Results showed that ۵۰% degradation were achieved within ۱۵ min.
کلیدواژه ها:
نویسندگان
azar bagheri
۱Department of Chemistry, Central Tehran Branch, Islamic Azad University, Tehran, Iran
hana amini
Chemistry, Central Tehran Branch, Islamic Azad University, Tehran, Iran
saeed raayati
۲Department of Chemistry, K. N. Toosi University of Technology, Tehran P. O. Box ۱۶۳۱۵-۱۶۱۸, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :