Investigation of optical and structural properties of iron oxide nanostructures synthesized by co-precipitation method
سال انتشار: 1401
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 60
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JOPN-7-3_006
تاریخ نمایه سازی: 25 بهمن 1402
چکیده مقاله:
In this research, iron oxide nanostructureshave been successfully synthesized using the coprecipitationmethod. The results of structural studiesusing X-ray diffraction (XRD) analysis showed that thesynthesized samples have a simple cubic structure. Thelattice parameter of these synthesized nanostructures wascalculated with the aid of the Rietveld refinementmethod. It was found that the lattice parameter is about۸.۳۸۸ Å. Electron microscopy images (SEM) showed thatthe samples have sheet likes shapes. From SEM images,it was found that the synthesized nanosheets' thicknesswas about ۳۳ nm. The optical properties of the sampleswere also studied using ultraviolet-visible spectroscopy.These studies showed that the samples have a broadabsorption peak of about ۳۵۰ nm. The samples wereirradiated with a beam with a wavelength of ۲۰۵ nm tomeasure the emission spectra. There were severalemission peaks observed in the emission spectra ofsamples. The highest emission peaks were observed at۴۸۲nm and ۵۲۷ nm, respectively.
کلیدواژه ها:
نویسندگان
Mostafa Arjomandi Lari
Department of Electrical Engineering, Dariun branch, Islamic Azad University, Dariun, Iran
saeed parhoodeh
Physics Department, Shiraz branch, Islamic Azad University, Shiraz, Iran
Ghader Alahverdi
Physics Department, Shiraz branch, Islamic Azad University, Shiraz, Iran & Department of Biochemistry, Fasa University of Medical Sciences, Fasa, Iran
Ali Rohani Sarvestani
Physics Department, Shiraz branch, Islamic Azad University, Shiraz, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :