Electrochemical performance of Nickel foam electrode in Potassium Hydroxide and Sodium Sulfate electrolytes for supercapacitor applications
سال انتشار: 1401
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 44
متن کامل این مقاله منتشر نشده است و فقط به صورت چکیده یا چکیده مبسوط در پایگاه موجود می باشد.
توضیح: معمولا کلیه مقالاتی که کمتر از ۵ صفحه باشند در پایگاه سیویلیکا اصل مقاله (فول تکست) محسوب نمی شوند و فقط کاربران عضو بدون کسر اعتبار می توانند فایل آنها را دریافت نمایند.
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JRCC-4-12_003
تاریخ نمایه سازی: 6 اسفند 1402
چکیده مقاله:
Nickel foam is a shallow-density metal part with very high electrical and thermal conductivity. Nickel foam is used widely as the current collector in electrochemical energy storage. In previous research, the electrolytes used for electrodes in energy sources in the laboratory are often of the aqueous electrolyte type due to their low cost and easy access. In this study, studies were performed to identify and confirm the accuracy of nickel foam, such as scanning electron microscopy and X-ray energy diffraction spectroscopy. Then, in common electrolytes, ۱ M potassium hydroxide (KOH) and ۰.۱ M sodium sulfate (Na۲SO۴) were investigated by CV, GCD, and EIS analyses. Finally, according to the data and results, the desired electrolyte can be selected depending on the type of use in different environments.Nickel foam is a shallow-density metal part with very high electrical and thermal conductivity. Nickel foam is used widely as the current collector in electrochemical energy storage. In previous research, the electrolytes used for electrodes in energy sources in the laboratory are often of the aqueous electrolyte type due to their low cost and easy access. In this study, studies were performed to identify and confirm the accuracy of nickel foam, such as scanning electron microscopy and X-ray energy diffraction spectroscopy. Then, in common electrolytes, ۱ M potassium hydroxide (KOH) and ۰.۱ M sodium sulfate (Na۲SO۴) were investigated by CV, GCD, and EIS analyses. Finally, according to the data and results, the desired electrolyte can be selected depending on the type of use in different environments.
کلیدواژه ها:
نویسندگان
Ehsan Niknam
Department of Materials Engineering, Tarbiat Modares University (TMU), Tehran, P.O. Box ۱۴۱۱۵-۱۴۳, Iran
Homam Naffakh-Moosavy
Department of Materials Engineering, Tarbiat Modares University (TMU), Tehran, P.O. Box ۱۴۱۱۵-۱۴۳, Iran
Majid Ghahraman Afshar
Chemistry and Process Engineering Department, Niroo Research Institute (NRI), Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :