AlFeO۳@SiO۲@SO۳H as a magnetic nanocatalyst for the synthesis of mono/bis-dihydropyrimidin-۲-ones and dihydropyridines as pharmaceutically active compounds
سال انتشار: 1402
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 39
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JRCC-5-14_002
تاریخ نمایه سازی: 6 اسفند 1402
چکیده مقاله:
In this research, the preparation of a reusable AlFeO۳@SiO۲@SO۳H nanostructure as a perovskite-based magnetic nanomaterial is described. The structure of prepared AlFeO۳@SiO۲@SO۳H was characterized by FT-IR, XRD, FE-SEM, EDS, TGA, and VSM analyses. The prepared acidic hybrid nanocatalyst showed high thermal stability and used as an efficient magnetic nanocatalyst in the synthesis of ۳,۴-dihydropyrimidin-۲-one, and mono/bis ۱,۴-dihydropyridine derivatives as pharmaceutically active heterocycles under solvent free conditions. High efficiency of procedure, good yields, short reaction times, magnetic recovery and reusability of nanocatalyst, high thermal stability of catalyst, and environmentally benign conditions are highlights of this new protocol.In this research, the preparation of a reusable AlFeO۳@SiO۲@SO۳H nanostructure as a perovskite-based magnetic nanomaterial is described. The structure of prepared AlFeO۳@SiO۲@SO۳H was characterized by FT-IR, XRD, FE-SEM, EDS, TGA, and VSM analyses. The prepared acidic hybrid nanocatalyst showed high thermal stability and used as an efficient magnetic nanocatalyst in the synthesis of ۳,۴-dihydropyrimidin-۲-one, and mono/bis ۱,۴-dihydropyridine derivatives as pharmaceutically active heterocycles under solvent free conditions. High efficiency of procedure, good yields, short reaction times, magnetic recovery and reusability of nanocatalyst, high thermal stability of catalyst, and environmentally benign conditions are highlights of this new protocol.
کلیدواژه ها:
نویسندگان
Mohammad Ali Bodaghifard
Department of Chemistry, Faculty of Science, Arak University, ۳۸۱۵۶-۸۸۱۳۸, Arak, Iran, AND Institute of Nanosciences and Nanotechnology, Arak University, ۳۸۱۵۶-۸۸۱۳۸, Arak, Iran
Najmieh Ahadi
Institute of Nanosciences and Nanotechnology, Arak University, ۳۸۱۵۶-۸۸۱۳۸, Arak, Iran
Faranak Ebrahimi
Department of Chemistry, Faculty of Science, Arak University, ۳۸۱۵۶-۸۸۱۳۸, Arak, Iran
Mahdia Hamidinasab
Department of Chemistry, Faculty of Science, Arak University, ۳۸۱۵۶-۸۸۱۳۸, Arak, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :