Evaluation of Hot Corrosion of Hot Dip Aluminized Coated Superalloy IN۷۳۸LC in Melted Na۲SO۴-۲۵wt% NaCl Salt
سال انتشار: 1403
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 14
نسخه کامل این مقاله ارائه نشده است و در دسترس نمی باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_PCBR-7-2_006
تاریخ نمایه سازی: 9 اردیبهشت 1403
چکیده مقاله:
Superalloy IN۷۳۸LC is categorized as one of the most frequently utilized nickel base superalloys in the production of hot section components due to its multiphase microstructure maximizing its strength under elevated temperatures. In this study, a hot dip diffusion coating of aluminum was employed on the nickel-base superalloy Inconel ۷۳۸LC substrate to enhance the hot corrosion resistance required for high-temperature applications, such as turbine blades. The aluminizing salt bath included Al powder with a particular composition, NaCl, KCl, Na۳AlF۶, and NaF. A thickness of about ۴۸ µm was attained by applying the coating for ۳۰ minutes at ۷۲۰ °C. Bare and aluminized coated specimens were subjected to hot corrosion assessment in molten salt, with a composition of Na۲SO۴-۲۵wt% NaCl at ۷۲۰ C being exposed for ۶۰ and ۱۴۰ hours. Scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and X-ray diffraction (XRD) were conducted on the coating sample to ensure the successful deposition of the hot dip aluminized layer. The aluminized sample exhibited excellent corrosion resistance owing to the formation of an Al۲O۳ layer, which meant that after ۱۴۰ hours of testing; very little coating deterioration was detected. In contrast, the naked sample suffered severe degradation and showed poor hot corrosion resistance. It was thought that the aluminized sample's superior hot corrosion resistance resulted from the uniform and dense growth of an Al۲O۳ protective scale without any cracks on the superalloy surface
کلیدواژه ها:
نویسندگان
Mohammad Sajjadnejad
Department of Materials Engineering, School of Engineering, Yasouj University, Yasouj, Iran
Vahid Tavakoli Targhi
Department of Materials and Metallurgical Engineering, Amirkabir University of Technology (Tehran Polytechnic), Tehran, Iran
Seyyed Mohammad Saleh Haghshenas
Department of Materials Science and Engineering, School of Engineering, Shiraz University, Shiraz, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :