The effect of particle size on photocatalytic degradation of oxytetracycline by ZnO nanoparticles
سال انتشار: 1403
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 29
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JWENT-9-2_005
تاریخ نمایه سازی: 30 اردیبهشت 1403
چکیده مقاله:
The toxicity of oxytetracycline (OTC) antibiotic remains in the environment and threatens the life of living things. In this research, two series of ZnO nanoparticle catalysts with different particle sizes were prepared.. The structural and optical characteristics of the samples were analyzed and the photocatalytic degradation of OTC was investigated under a ۱۰۰ W visible light irradiation. The samples prepared using zinc nitrate and zinc acetate showed different photocatalytic performance. The catalysts prepared at lower calcination temperatures show higher photocatalytic performance due to the active surface of the particles. The intensity of the peaks in the XRD patterns of samples also increases with increasing calcination temperature, which confirms the increase in the size of the nanoparticles. The decrease in particle size with increasing calcination temperature was confirmed by FESEM images. On the other hand, the band gap energy was reduced by decreasing the calcination temperature, which increases the performance of the photocatalytic activity. The ۲۷ nm ZnO nanoparticles prepared using zinc nitrate showed ۱۰۰ % degradation efficiency. As a result, we reached the maximum performance of pure ZnO by only controlling the size and morphology, without making nanocomposite or doping different elements. google is broken
کلیدواژه ها:
نویسندگان
Reza Torkamani
Faculty of Physics, University of Tabriz, Tabriz, Iran
Bagher Aslibeiki
Faculty of Physics, University of Tabriz, Tabriz, Iran
Masih Darbandi
Nanomaterials Research Laboratory, Department of Physical Chemistry, Faculty of Chemistry, University of Tabriz, Tabriz, Iran
Hamid Naghshara
Faculty of Physics, University of Tabriz, Tabriz, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :