Extraction and Characterization of Alginate from Sargassum angustifolium collected from northern coasts of Persian Gulf, Bushehr
سال انتشار: 1391
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 2,071
فایل این مقاله در 5 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
SASTECH07_143
تاریخ نمایه سازی: 30 تیر 1392
چکیده مقاله:
Alginates, unbranched polymers of polysaccharide with gel forming properties made up by blocks of beta-(1-4)-d-mannuronic acid (M) and alpha-(1-4)-l-guluronic acid (G), have emerged as valuable biomaterials with interesting biomedical and biotechnological applications. In brown seaweeds, alginates are the most abundant polysaccharides reaching up to 40% of the dry weight. The extraction of alginate may be regarded as a process in two steps: transformation of insoluble alginate into a soluble form namely sodium alginate, followed by diffusion of the soluble glycuronan into solution.Alginate fractions from Sargassum angustifolium brown seaweed were extracted after collection, washing, drying and grinding of seaweeds into powder, and then characterized by 1HNMR and rheological measurements. 1HNMR spectroscopy is most suitable for characterizing both the composition and the distribution sequence of the two uronate residues in algal samples.The alginate extraction conditions were investigated. In the optimized condition, samples extracted for 3×3h at 50ºC were further purified by re-precipitation with ethanol. The M/G ratio value was 0.89, higher than the ratio for most Sargassum species alginates. The homopolymeric blocks FGG and FMM of these fractions characterized by 1HNMR spectroscopy were 0.39 and 0.33, respectively (η<1). Therefore, the alginate from S. angustifolium is much richer in mannuronic block structures than those from other Sargassum species. Values of Mw for alginate samples were also calculated using intrinsic viscosity data. The Mw value was 702.6 kDa.
کلیدواژه ها:
نویسندگان
S Gholamipoor
Khorramshahr University of Marine Science and Technology
Y Nikpour-Ghanavati
Department of Marine Chemistry, Faculty of Marine Science, Khorramshahr University of Marine Science and Technology, Khorramshahr, Iran;
A.R Oromie bie
IPPI & Khatam Polymer co., Tehran, Iran
M Mohammadi
Department of Marine biotechnology, Persian Gulf Research and Studies Center, Persian Gulf University, Bousheher, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :