Fabrication of magnesium fluoridated hydroxyapatite nanoparticle-polycaprolactone nanocomposite via electrospinning
محل انتشار: نوزدهمین کنفرانس مهندسی پزشکی ایران
سال انتشار: 1391
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 857
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICBME19_051
تاریخ نمایه سازی: 9 بهمن 1392
چکیده مقاله:
The electrospinning technique provides non-wovens to the order of few nanometers with large surface areas, ease of functionalisation for various purposes and superior mechanical properties. Also, the possibility of large scale productions combined with the simplicity of the process makes this technique very attractive for many different applications. However, a key precondition is the ability to obtain bead-free fibres with diameters in the nanoscale range. At present the most normally used solvent for electrospinning PCL is chloroform, but this only leads to fibres in the microscale range. Consequently various solvent systems were studied in this study. The solvent mixture ethanol/chloroform was found to allow for nanofibers with a diameter several times smaller than the solvent chloroform. Also, it is hypothesized that magnesium fluoridated hydroxyapatite nanoparticles - poly (ε-caprolactone) (PCL) nanocomposite tissue scaffolds can be made more bioactive by using magnesium fluoridated hydroxyapatite nanoparticle. Increasing content of magnesium in structure changes degradation rate. The overall objective of this study is to fabricate and characterize electrospun magnesium fluoridated hydroxyapatite nanoparticle - poly (ε- caprolactone) (PCL) nanocomposite scaffold as substrates for bone tissue engineering. The electrospun nanocomposite was characterized by SEM, XRD, TEM and Mechanical testing.
کلیدواژه ها:
nanocomposite ، magnesium fluoridated hydroxyapatite nanoparticle ، electrospinning ، tissue engineering
نویسندگان
Z Fereshteh
Department of Materials Engineering Isfahan University of Technology (IUT) Esfahan, ۸۴۱۵۶-۸۳۱۱۱, IRAN
M. H. Fathi
Department of Materials Engineering Isfahan University of Technology (IUT) Esfahan, ۸۴۱۵۶-۸۳۱۱۱, IRAN.
R Mozaffarinia
Faculty of Materials Science and Engineering Malek Ashtar University of Technology Shahin Shahr, IRAN