Laboratory Study on Mechanical Strength and Mix Proportions of RCC Pavements in Cold Regions
سال انتشار: 1392
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 865
فایل این مقاله در 11 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICCAU01_3144
تاریخ نمایه سازی: 29 تیر 1393
چکیده مقاله:
Roller compacted concrete (RCC) has recently been used as an alternative to conventional concrete as industrial and heavy duty pavements. Benefits of RCC were discussed as a cost-effective type of pavements. In order to evaluate freeze-thaw resistance of specimens more accurate and reliable, gyratory compactor was used. Generally, three mix designs with different water to cement ratios were prepared with 12 cylinderical samples for each mixture. Freeze-thaw durability of mixtures after sawn to prisms was evaluated by mass loss percent which was according to the ASTM C666 Procedure (A) method. Results have shown that freeze thaw resistance of RCC specimens is more depended to cement paste and water to cement ratio, and then the degree of compaction. Splitting tensile strength is related to cohesiveness between cement paste and aggregate which can predict the freeze thaw durability of RCC pavement samples. Range of tensile strength at the same maximum number of freeze-thaw cycle for high cement paste with high durability have not shown significant different as gyrations changed from 50 to 90
کلیدواژه ها:
نویسندگان
ReyhanehSadat Shahangian
Assistant Professor,Islamic Azad University,South Tehran Branch
Kianoush Siamardi
M.Sc Student,Transportation Engineering, Islamic Azad University, South Tehran Branch
Omid Rahmani
M.Sc Student,Transportation Engineering, Islamic Azad University, South Tehran Branch
Mohamad Jalal
M.Sc Student,Transportation Engineering, Islamic Azad University, South Tehran Branch
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :