The evaluation of dynamical-mechanical and theramal properties of Polycarbonate/carbon nanotubes (CNTs) nanocomposites
سال انتشار: 1395
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 614
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
CHCONF02_017
تاریخ نمایه سازی: 9 مرداد 1395
چکیده مقاله:
The objective of this study is the effect of carbon nanotubes (CNT) functionalized in different percentage of dispersion on the morphology, Dynamical-mechanical and thermal properties of Nanocomposites of PC/CNT. The Nanotubes that used in this study have diameter between 10-20 nm and the average length of Nanotubes is 10μm. Moreover, the Nanotubes had been functionalized by Carboxylic functional group. The composites were obtained by solvent evaporation. The results of TEM test, dynamic-mechanical and thermal properties proved, the amount of mixing, dispersion and distribution of the carbon nano tubes case to improve the Nanocomposite properties. The TEM test results showed that, increasing the amount of Nano-particles from 0.5 wt. % to 5 wt. % causes to have better dispersion of Nanocomposite on the nano-material surface. TGA tests were used to investigate the thermal properties of the Nano-composites. The results showed that increasing the percentage of nanotubes can be increased the destruction temperature. DMTA test was used to investigate the mechanical-dynamical properties. As expected, increasing in the amount of nanotubes causes to increase the amount of storage modulus. Meanwhile, Tanδ decreased with increasing the nanotube and elastic module.
کلیدواژه ها:
نویسندگان
Mohammadreza Kamrani Moghadam
Polymer science and engineering department, Islamic Azad University, Shiraz-Iran
Alireza Aghili
Associate Professor, Polymer science and engineering department, Islamic Azad University, Shiraz-Iran
Shahram Moazami
Polymer science and engineering department, Islamic Azad University, Shiraz-Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :