Synthesis of SrCO3 nano-powder from Celestite ore by mechanical milling
محل انتشار: دهمین همایش مشترک و پنجمین کنفرانس بین المللی انجمن مهندسی مواد و متالورژی و انجمن علمی ریخته گری ایران
سال انتشار: 1395
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 429
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES10_170
تاریخ نمایه سازی: 6 اردیبهشت 1396
چکیده مقاله:
In the present investigation, strontium carbonate nano-powder was synthesized by mechano-chemical reaction of celestite (natural ore of strontium) and sodium carbonate during high energy mechanical milling. A planetary ball mill operated for different durations up to 16 hours and various Na2CO3:SrSO4 molar ratios of 1.05:1, 1.15:1 and 1.25:1. X-Ray diffraction (XRD) analysis and Scanning electron microscope (SEM) analysis have been used for characterization. XRD analysis showed that in a Na2CO3:SrSO4 molar ratio of 1.05:1, mechano-chemical reaction started within less than 1 hour of milling and the amount of conversion increased on increasing milling time and it has not been completed after 16 hours of milling. However, by increasing the molar ratio of Na2CO3:SrSO4 to 1.25:1, the SrCO3 formation was completed up to 2 hours of milling. The results also showed that the mean crystallites sizes of produced nano-powder were less than 50 nm. SEM results showed that the final product consisted of spherical particles and the agglomerates included SrCO3 nano particles with the mean size of 80 nm.
کلیدواژه ها:
نویسندگان
Erfan Alimohammadi
M.Sc. student of Metallurgy and Materials Engineering
Saeed Sheibani
Assistant Professor of Metallurgy and Materials Engineering School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran, Iran
Abolghasem Ataie
Professor of Metallurgy and Materials Engineering School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :