Characterization of copper ferrite spinel synthesized by glycinenitrate combustion process for using as solid oxide fuel cell interconnects coating
محل انتشار: سومین کنفرانس هیدروژن و پیل سوختی
سال انتشار: 1394
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 472
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
H2FC03_014
تاریخ نمایه سازی: 19 خرداد 1396
چکیده مقاله:
In this research, CuFe2O4 spinel powder was prepared by an optimized glycine-nitrate combustion process (GNP) followed by calcinations. The samples were characterized by X-ray diffraction (XRD), scanningelectron microscopy (SEM), dilatometry and 4-probe DC methods. Different glycine to nitrate (G/N) ratios of 1(fuel-deficient), 1.48 (stoichiometric) and 2 (fuel-rich) were employed. The as-prepared powders were calcinedat 800 and 1000 °C for 5 hours. It showed that the 2 ratio resulted in the formation of desired copper spinel single phase at both calcinations temperatures. The electrical conductivity and the coefficient of thermalexpansion of the sintered pelletized samples were obtained 2 S.cm-1 (800°C) and 11×10-6 °C-1 (25-800°C), respectively.
کلیدواژه ها:
نویسندگان
s.n hosseini
Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111, Iran
f karimzadeh
Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111, Iran
m.h. Enayati
Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :