Theoretical models for prediction of mechanicalbehaviour of the PP/EPDM nanocomposites fabricatedby friction stir process
محل انتشار: فصلنامه پلی اولفین ها، دوره: 4، شماره: 1
سال انتشار: 1395
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 509
فایل این مقاله در 11 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_POJ-4-1_003
تاریخ نمایه سازی: 29 آذر 1396
چکیده مقاله:
In this study, thermoplastic polyolefn elastomeric (TPO) nanocomposites were fabricated by friction stir processing. The effect of different pin geometries on clay dispersion and mechanical properties of the TPOnanocomposite reinforced with 3% wt nanoclay has been frst investigated. The optimum pin geometry namelythreaded cylindrical pin was then used to fabricate the nanocomposites containing 3, 5 and 7 wt% nanoclay.The results showed that increase in the clay content increased the tensile strength and tensile modulus of thenanocomposite from 15.8 to 22.76 MPa and 568 to 751 MPa, respectively. The experimental stress – strain curvesof nanocomposites were compared with eight constitutive models including Mooney – Rivlin, the second-orderpolynomial, Neo – Hookean, Yeoh, Arruda – Boyce, Van der Waals and the third- and sixth-order Ogden. Thecomparisons showed that there was an agreement between the experimental data and the sixth-order Ogden model.Three micromechanical models Halpin – Tsai, inverse rule of mixture and linear rule of mixture were applied toinvestigate the Young’s modulus of nanocomposites. Because of the signifcant difference between the Young’smodulus obtained from these models and the ones obtained from experimental data, a modifying factor was used toimprove the theoretical predictions obtained from the models. Polyolefns J (2017) 4: 99-109
کلیدواژه ها:
نویسندگان
Amir Mostafapour
Faculty of Mechanical Engineering, University of Tabriz, Tabriz, Iran
Ghasem Naderi
Faculty of Polymer Processing, Iran Polymer and Petrochemical Institute (IPPI), Tehran, Iran
Mohammad Reza Nakhaei
Faculty of Mechanical Engineering, University of Tabriz, Tabriz, Iran