EFFECT OF CASTING TEMPERATURE ON THE RISK OF CRACKING IN THE MASS CONCRETE COLUMNS CONTAIN SILICA FUME
محل انتشار: سومین کنفرانس بین المللی بتن و توسعه
سال انتشار: 1388
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,876
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICCD03_049
تاریخ نمایه سازی: 20 مهر 1387
چکیده مقاله:
In this paper the effect of different casting temperatures on cracking potential of mass high strength columns were studied. Four mix proportions with 0.3 watercementing ratio were made and two different casting temperatures, 26ºC and 40ºC were applied to simulate moderate and hot climate conditions. Cement was replaced by silica fume at 0%, %5, %8 and %11. Temperature rising of the mixtures, due to hydration, after casting was monitored till 7 days. Furthermore, compressive strength of the specimens was determined at the ages of 1 to 91 days. Thermal analysis of 4 large columns, 600×600×200 to 1800×1800×2000 mm, was carried out by finite element method [3-7]. In this regard, two demolding time, 24 and 48 hours were selected to clarify the effect of ambient temperature on risk of cracking. The results declare that tensile stress of the 600 mm columns with 24 hours demolding time, irrespective of casting temperature, was higher than tensile strength and will be cracked. However, 48 hours demolding time induced lower tensile stress and diminished risk of cracking. Silica fume has no considerable effect on risk of cracking.
کلیدواژه ها: